Method for hydroentangling non-woven fibrous sheets
Assignee: Dexter Corp
•
Filing: 1990-06-01
•
Granted: —
•
Expires: 2010-06-01
Abstract
Abstract A method for hydroentangling nonwoven fibrous sheet material to significantly increase the strength thereof at low latex add-on values employs small diameter jets of high-pressure water in the form of coherent streams that concentrate the hydraulic energy over a distance equal to approximately the diameter of the fibers being entangled. While fiber entangling water jets have been utilized heretofore, the present invention employs a relatively lower pressure for the fiber rearrangement along with a synergistic effect of wood pulp and long polyester fibers coupled with small amounts of latex to achieve the unexpectedly high strengths within these light weight materials. The resultant sheet material possesses excellent uniformity of fiber distribution and improved strength characteristics over those typically obtained from prior art water jet entanglement processes requiring 300-2000% the entanglement input energy employed in this process.
Inventors
- 👤 Helen Viazmensky
- 👤 Carl E. Richard
- 👤 James E. Williamson
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-04 11:04
CPC Classifications
D; D21; D21H; D21H13/00; D21H13/10; D21H13/12; D21H13/14; D04; D04H; D04H1/00; D04H1/40; D04H1/44; D04H1/46; D04H1/48; D04H1/49; D21H13/20; D21H13/24; D21H15/00; D21H15/02; D21H15/06; D21H25/00; D21H25/005
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
156 words
A method of producing a fiber entangled nonwoven web material comprising the steps of forming a dilute homogeneous fiber furnish of papermaking fibers and more than about 30 percent by weight of long synthetic fibers suited for being dispersed in an aqueous media; depositing the fibers from the furnish on a paper forming wire at the wet end of a papermaking machine to provide a fluidized homogeneously dispersed fibrous base web material having a fluid content of about 75% by weight or more; subjecting the fibrous base web having said fluid content to a series of entangling fluid jets to provide a total energy input of up to about 0.2 hp-hr/lb to very lightly entangle the fibers in said base web; drying the entangled web and treating the web with a binder in an amount sufficient to provide a binder pickup of less than about 20% by weight based on the weight of the treated material.
Claim 2
Independent Claim
156 words
A method of producing a fiber entangled nonwoven web material comprising the steps of forming a dilute homogeneous fiber furnish of papermaking fibers and more than about 30 percent by weight of long synthetic fibers suited for being dispersed in an aqueous media; depositing the fibers from the furnish on a paper forming wire at the wet end of a papermaking machine to provide a fluidized homogeneously dispersed fibrous base web material having a fluid content of about 75% by weight or more; subjecting the fibrous base web having said fluid content to a series of entangling fluid jets to provide a total energy input of up to about 0.2 hp-hr/lb to very lightly entangle the fibers in said base web; drying the entangled web and treating the web with a binder in an amount sufficient to provide a binder pickup of less than about 20% by weight based on the weight of the treated material.
Claim 3
Dependent Claim
23 words
The process of claim 1 wherein said fibrous base web is being carried by said paper-forming wire at the time it is entangled.
Claim 4
Dependent Claim
15 words
The process of claim 1 wherein the fiber furnish comprises about 10-60 percent natural fibers.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein the synthetic fiber content is about 50-80% by weight.
Claim 6
Dependent Claim
20 words
The process of claim 1 wherein the synthetic fibers have a fiber length in the range of about 15-30 mm.
Claim 7
Dependent Claim
19 words
The process of claim 1 wherein the total energy input falls in the range of 0.01 to 0.15 hp-hr/lb.
Claim 8
Dependent Claim
19 words
The process of claim 1 wherein the total energy input falls in the range of 0.05 to 0.12 hp-hr/lb.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein the series of entangling jets include plural manifolds of nozzles having an orifice size within the range of 0.05-0.2 mm.
Claim 10
Dependent Claim
20 words
The process of claim 8 wherein the nozzles in each manifold are spaced by a distance of about 0.2-10 mm.
Claim 11
Dependent Claim
22 words
The process of claim 1 wherein the entangling fluid jets are operated at a pressure of about 20-70 kilograms per square centimeter.
Claim 12
Dependent Claim
30 words
The process of claim 1 wherein the binder is applied as a latex dispersion in quantities sufficient to provide a pickup of about 3 to 15 percent by weight binder.
Claim 13
Dependent Claim
14 words
The process of claim 11 wherein the the binder is a cross-linkable acrylic material.
Claim 14
Dependent Claim
15 words
The process of claim 11 wherein the binder is applied uniformly to the base web.
Claim 15
Dependent Claim
9 words
The product obtained from the method of claim 1.
Claim 16
Dependent Claim
9 words
The product obtained from the method of claim 7.
Claim 17
Dependent Claim
9 words
The product obtained from the method of claim 11.