Laminated polyester film

Assignee: Diafoil Co Ltd
•
Filing: 1989-09-18
•
Granted: —
•
Expires: 2009-09-18
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Disclosed herein is a laminated film comprising a polyester film containing minute closed cells and having a density of 0.40 to 1.30 g/cm³ and a polyester film having a density of more than 1.30 g/cm³ laminated on one side or both sides of the polyester film containing minute closed cells. In the laminated film of the present invention, the surface smoothness, which is a serious defect of a conventional film containing a large number of minute closed cells, is improved and the ink adhesive property is also improved, thereby enhancing the printing suitability. The breakage during the stretching process of film formation is reduced and the film forming properties are improved. Thus, the productivity was enhanced, thereby enabling the film to be supplied to the market at a low cost. Application of the film to various fields is enabled and the industrial value of the film is very large.

Inventors

  • 👤 Satoshi Otonari
  • 👤 Yoshinori Sato
  • 👤 Narihiro Masuda
  • 👤 Kazuyuki Akatsu

Bibliographic Details

Application Number —
Jurisdiction EP
Data Source google_patents
Last Synchronized 2026-11-03 19:24
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/18; B32B27/00; B32B27/36; B32B27/06; B32B27/065; B32B27/08; C; C08; C08J; C08J5/00; C08J5/18; B32B2367/00; C08J2367/00; C08J2367/02

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 55 words
A laminated film comprising a uniaxially or biaxially stretched polyester film containing minute closed cells and having a density of 0.40 to 1.30 g/cm³ and a uniaxially or biaxially stretched polyester film having a density of more than 1.30 g/cm³ laminated on one side or both sides of said polyester film containing minute closed cells.
Claim 2
Dependent Claim 55 words
A laminated film comprising a uniaxially or biaxially stretched polyester film containing minute closed cells and having a density of 0.40 to 1.30 g/cm³ and a uniaxially or biaxially stretched polyester film having a density of more than 1.30 g/cm³ laminated on one side or both sides of said polyester film containing minute closed cells.
Claim 3
Dependent Claim 35 words
A laminated film according to claim 1, wherein said polyester film having a density of 0.40 to 1.30 g/cm³ comprises a polyester and 3 to 40 wt% of a crystalline polypropylene based on said polyester.
Claim 4
Dependent Claim 21 words
A laminated film according to claim 2, wherein said polypropylene have a melt flow index of 0.2 to 120 g/10 min.
Claim 5
Dependent Claim 19 words
A laminated film according to claim 1, wherein the density of said laminated film is 0.50 to 1.37 g/cm³.
Claim 6
Dependent Claim 21 words
A laminated film according to claim 1, wherein the air leakage index of said laminated film is 1000 to 10000 sec.
Claim 7
Dependent Claim 33 words
A laminated film according to claim 1, wherein the center-line averaged surface roughness on the surface of said polyester film having a density of more than 1.30 g/cm³ is 0.05 to 1.0 µm.

References Cited (Backward Citations)

No citation records indexed.

USPTO Annuity & Maintenance Windows

Maintenance schedule is calculated for granted US utility patents.

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag