A method for preparing filled silicone rubber particles
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1988-11-29
•
Granted: —
•
Expires: 2008-11-29
Abstract
Abstract Cured silicone rubber powder containing large amounts of particulate material formed by dispersing a liquid silicone rubber composition curable by a platinum-catalyzed hydrosilation reaction into water. The presence of a low molecular weight, volatile polydiorganosiloxane makes it possible to incorporate at least 100 parts by weight of particulate material per 100 parts of curable polydiorganosiloxane into the composition. The volatile polydiorganosiloxane is removed from the cured powder. Finely divided magnetic metals, electrically conductive materials and reinforcing silica powders can be incorporated using the present method.
Inventors
- 👤 Saito Masayuki
- 👤 Mitsuo Hamada
- 👤 Yoshida Keiji
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-04 15:51
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/205; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/22; C08G77/24; C08G77/70; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
191 words
In a method for preparing a highly filled silicone rubber powder, said method comprising dispersing into water maintained at a temperature of at least 25° C. a liquid silicone rubber composition comprising (A) 100 weight parts of an organopolysiloxane having at least 2 lower alkenyl groups in each molecule, (B) an organohydrogenpolysiloxane having at least 3 silicon-bonded hydrogen atoms, where the molar ratio of silicon-bonded hydrogen atoms to the total concentration of lower alkenyl groups in ingredient (A) is from 0.5 to 20, respectively, (C) an amount of a platinum compound equivalent to from 0.1 to 1,000 parts by weight of platinum per 1,000,000 parts of combined weight of ingredients (A) and (B), and (D) a microparticulate powder having an average particle diameter not exceeding 20 micrometers, the improvement comprising (1) the addition to said liquid silicone rubber composition of (E) from 20 to 2,000 weight parts of an unreactive, volatile diorganopolysiloxane having a degree of polymerization not exceeding 10, and from 100 to 1000 parts by weight of said microparticulate powder (D) per 100 parts of said composition and (2) subsequently drying the resultant cured powder to remove ingredient (E).
Claim 2
Dependent Claim
191 words
In a method for preparing a highly filled silicone rubber powder, said method comprising dispersing into water maintained at a temperature of at least 25° C. a liquid silicone rubber composition comprising (A) 100 weight parts of an organopolysiloxane having at least 2 lower alkenyl groups in each molecule, (B) an organohydrogenpolysiloxane having at least 3 silicon-bonded hydrogen atoms, where the molar ratio of silicon-bonded hydrogen atoms to the total concentration of lower alkenyl groups in ingredient (A) is from 0.5 to 20, respectively, (C) an amount of a platinum compound equivalent to from 0.1 to 1,000 parts by weight of platinum per 1,000,000 parts of combined weight of ingredients (A) and (B), and (D) a microparticulate powder having an average particle diameter not exceeding 20 micrometers, the improvement comprising (1) the addition to said liquid silicone rubber composition of (E) from 20 to 2,000 weight parts of an unreactive, volatile diorganopolysiloxane having a degree of polymerization not exceeding 10, and from 100 to 1000 parts by weight of said microparticulate powder (D) per 100 parts of said composition and (2) subsequently drying the resultant cured powder to remove ingredient (E).
Claim 3
Dependent Claim
116 words
A method according to claim 1 where the concentration of said organohydrogensiloxane is equivalent to from 1.05 to 5 silicon-bonded hydrogen atoms per alkenyl group, the concentration of said platinum compound is equivalent to from 1 to 100 parts by weight of platinum per million parts of the combined weight of said organopolysiloxane and said organohydrogensiloxane, the concentration of said microparticulate powder is from 200 to 700 parts by weight per 100 parts of said organopolysiloxane, the water into which said curable composition is dispersed contains a surfactant and the temperature of said water is at least 50° C., and said water is set in motion to provide a flow rate of at least 0.1 cm./second.
Claim 4
Dependent Claim
101 words
A composition according to claim 1 where the alkenyl groups of said organopolysiloxane are vinyl and the remaining organic groups are methyl or a combination of methyl with either phenyl or 3,3,3-trifluoropropyl, the organic groups of said organohydrogensiloxane are methyl or a combination of methyl with either phenyl or 3,3,3-trifluoropropyl, said unreactive organopolysiloxane is a cyclic or linear dimethylpolysiloxane, said platinum compound is chloroplatinic acid, a solution of chloroplatinic acid in an alcohol or ketone, or a complex of chloroplatinic acid and an olefin, and said microparticulate powder is a magnetic metal powder, an electrically conductive powder or a reinforcing filler.