Process for bonding and stretching nonwoven sheet
Assignee: EIDP Inc
•
Filing: 1987-02-27
•
Granted: —
•
Expires: 2007-02-27
Abstract
Abstract Fibrous polyolefin nonwoven sheets are bonded and stretched in a continuous, multiple stage process. First, the sheet is heated without significant stretching to a temperature that is close to, but below, the melting temperature of the polyolefin. Then, as the sheet is forwarded to a first stretching stage, the sheet temperature is decreased by 5 to 40°C and thereafter the sheet is alternately heated and cooled as it passes through successive stretching stages, before final cooling to below 60°C. In comparison to similar sheets bonded and stretched at constant temperature, the sheets produced by the process of the present invention are significantly more uniform in thickness.
Inventors
- 👤 Hyun Sung Lim
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-04 14:55
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/08; D04H3/10; D04H1/00; D04H1/40; D04H1/54; D04H3/005; D04H3/007
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
136 words
A continuous process for bonding and stretching a fibrous polyolefin nonwoven sheet wherein the sheet is first heated to a bonding temperature that is near but below the melting point of the polyolefin, then is stretched in at least two stages to at least 1.2 times its original length and then is cooled to a temperature below 60°C, and wherein forces are applied perpendicular to the sheet surface during the heating, stretching and cooling when the sheet temperature is at 100°C or higher, characterised in that the sheet temperature is decreased by 5 to 40°C immediately after the sheet is heated to the bonding temperature and as the sheet is being forwarded to a first stretching stage, and in that the sheet is then alternately heated and cooled in subsequent stretching stages of the continuous process.
Claim 2
Dependent Claim
136 words
A continuous process for bonding and stretching a fibrous polyolefin nonwoven sheet wherein the sheet is first heated to a bonding temperature that is near but below the melting point of the polyolefin, then is stretched in at least two stages to at least 1.2 times its original length and then is cooled to a temperature below 60°C, and wherein forces are applied perpendicular to the sheet surface during the heating, stretching and cooling when the sheet temperature is at 100°C or higher, characterised in that the sheet temperature is decreased by 5 to 40°C immediately after the sheet is heated to the bonding temperature and as the sheet is being forwarded to a first stretching stage, and in that the sheet is then alternately heated and cooled in subsequent stretching stages of the continuous process.
Claim 3
Dependent Claim
73 words
A process as claimed in claim 1 wherein the nonwoven sheet is formed of flash-spun, plexifilamentary film-fibril strands of linear polyethylene, the bonding temperature is within 3 to 8°C below the melting point of the polyethylene, the sheet has a unit weight before stretching in the range of 35 to 70 g/m 2 , and the sheet is stretched longitudinally in two or three stages to 1.2 to 1.7 times its original length.
Claim 4
Dependent Claim
35 words
A process as claimed in claim 1 or claim 2 wherein the sheet temperature is decreased from the bonding temperature by 10 to 25°C as the sheet is being forwarded to the first stretching stage.
Claim 5
Dependent Claim
43 words
A process as claimed in any one of claims 1 to 3 wherein the alternate heating and cooling during the subsequent stretching increases the sheet temperature to no higher than the bonding temperature and decreases the sheet temperature to no lower than 100°C.
Claim 6
Dependent Claim
32 words
A prooess as claimed in any one of the preceding claims wherein the sheet temperature during the alternate heating and cooling varies by at least 5°C but by no more than 35°C.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 5 wherein the sheet temperature during the alternate heating and cooling varies by 10 to 25°C.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.