EP0203469A1
Expired / Lapsed
EP
⏱️ 0.0 years remaining
Improved polyester fiberfill and process
Assignee: advansa Bv
•
Filing: 1986-05-15
•
Granted: —
•
Expires: 2006-05-15
Abstract
Abstract Polyester fiberfill having spiral-crimp that is randomly-arranged and entangled in the form of fiberballs with a minimum of hairs extending from their surface, and having a refluffable characteristic similar to that of down on account of the low cohesion between the balls. a process for making such fiberballs by repeatedly air-tumbling small tufts of such fiberfill against the wall of a vessel.
Inventors
- 👤 Ilan Marcus
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-05 04:01
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/02; A; A47; A47G; A47G9/00; B; B68; B68G; B68G1/00; D04H1/40; D04H1/42; D04H1/4326; D04H1/435; D04H1/4391; D04H1/43918; D04H1/54; D06; D06M; D06M15/00; D06M15/19; D06M15/37; D06M15/507; B68G2001/005; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2904; Y10T428/2907; Y10T428/2909; Y10T428/2913; Y10T428/2922; Y10T428/2924; Y10T428/2929; Y10T428/2931; Y10T428/2933; Y10T428/2962; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/2982; Y10T428/31504; Y10T428/31652; Y10T428/31663
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
41 words
Refluffable fiberballs of average dimension 1 to 15 mm, consisting essentially of randomly-arranged, entangled, spirally-crimped polyester fiberfill having a cut length of about 10 to about 60 mm, and having a cohesion measurement as defined of less than 6 Newtons (N).
Claim 2
Dependent Claim
41 words
Refluffable fiberballs of average dimension 1 to 15 mm, consisting essentially of randomly-arranged, entangled, spirally-crimped polyester fiberfill having a cut length of about 10 to about 60 mm, and having a cohesion measurement as defined of less than 6 Newtons (N).
Claim 3
Dependent Claim
15 words
Fiberballs according to Claim 1, wherein the cohesion measurement is about 4.5 N or less.
Claim 4
Dependent Claim
30 words
Fiberballs according to Claim 1, wherein at least 50% by weight of the balls have a cross-section such that its maximum dimension is not more than twice its minimum dimension.
Claim 5
Dependent Claim
27 words
Fiberballs according to Claim 1, wherein the fiberfill is coated with a silicone slickener in amount about 0.1 to about 0.5% Si by weight of the fiberfill.
Claim 6
Dependent Claim
20 words
Fiberballs according to Claim 4, wherein the amount of silicone is 0.3 to 0.4% Si by weight of the fiberfill.
Claim 7
Dependent Claim
14 words
Fiberballs according to Claim 1, wherein the fiberfill is of denier 1 to 10.
Claim 8
Dependent Claim
18 words
Blends of fiberballs according to Claim 6, intimately blended with staple fibers of denier significantly higher than 10.
Claim 9
Dependent Claim
25 words
Blends of fiberballs according to Claim 1, intimately blended with pieces of light-weight non-woven fabrics in amount 5 to 30% by weight of the blend.
Claim 10
Dependent Claim
13 words
Blends of fiberballs according to Claim 1, intimately blended with down and/or feathers.
Claim 11
Dependent Claim
21 words
Fiberballs according to Claim 1, packed into bags like down, so that the fiberballs may be removed and transported by suction.
Claim 12
Dependent Claim
29 words
Fiberballs according to Claim 1, compressed into packages of density up to about 100 Kg/m 3 , and such that the fiberballs may be removed and transported by suction.
Claim 13
Dependent Claim
44 words
Process for making polyester fiberfill having refluffable characteristics, wherein small tufts of polyester fiberfill having spiral-crimp are repeatedly tumbled by air against the wall of a vessel to provide an assembly of fiberballs having a cohesion value as defined of less than 6 N.
Claim 14
Dependent Claim
44 words
Process for making polyester fiberfill having refluffable characteristics, wherein small tufts of polyester fiberfill having spiral-crimp are repeatedly tumbled by air against the wall of a vessel to provide an assembly of fiberballs having a cohesion value as defined of less than 6 N.
Claim 15
Dependent Claim
30 words
Process according to Claim 12, wherein the tufts are tumbled against a cylindrical wall of a vessel by air stirred by blades attached to shaft rotating axially in the vessel.
Claim 16
Dependent Claim
17 words
Process according to Claim 13, wherein the small tufts and the air are recirculated through the vessel.
Claim 17
Dependent Claim
36 words
Process according to Claim 12, wherein the tufts are formed by feeding loose fiberfill into the vessel, and rotating the shaft and blades at a speed such that the fiberfill is separated into the small tufts.
Claim 18
Dependent Claim
26 words
Process according to Claim 12, wherein small tufts that are not elongated are formed before feeding them into the vessel for rounding and condensing by air-tumbling.
Claim 19
Dependent Claim
30 words
Process according to Claim 12, wherein the tufts formed in the vessel are treated with a polysiloxane slickener, and the cohesion value is reduced to about 3 N or less.
Claim 20
Dependent Claim
18 words
Process according to Claim 12, wherein the cohesion value of the assembly is about 4.5 N or less.
References Cited (Backward Citations)
US3454422A
Cited
US4065599A
Cited
US3892909A
Cited
DE2349235A1
Cited
US4259400A
Cited
DE2751689A1
Cited
US4144294A
Cited
US4418103A
Cited
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.