Porous mullite

Abstract

Abstract Clay, preferalby kaolin, is calcined through its exotherm, but without substantial mullite formation [e.g., 1 hour at 1000°C]. The calcined clay is leached with an alkaline aqueous solution to remove [i.e., leach] silica. If the molar A1 2 0 3 /Si0 2 ratio is < 3/2 the final product will contain mullite plus excess SiO 2 and if the A1 2 0 3 /Si0 2 ratio is < 3/2, the final product will contain excess Al 2 O 3 . The leached clay is washed, preferably under acid conditions at about pH 3-5, to remove excess alkali ions; and then dried. The washed clay is then calcined at conditions to produce mullite [e.g., 3 hours at 1250°F]. Materials made in this manner exhibit high pore volume despite the final high temperature heat treatment and suitable for catalyst and sorbent applications.