Silicone rubber as modifier for Poly(Arylene Sulfide)
Assignee: Phillips Petroleum Co
•
Filing: 1984-11-15
•
Granted: —
•
Expires: 2004-11-15
Abstract
Abstract A composition and method for forming the composition providing a molding composition of poly(arylene sulfide) and a crack resistance and/or an impact strength improving amount of a polymeric rubber chosen from among silicone rubber, ethylene-acrylic rubber, ethylene-propylene rubber, ethylene-propylene-diene rubber, and poly(butyl acrylate) rubber. In embodiments of the invention the improvement is enhanced by the addition of organosilane to the composition.
Inventors
- 👤 William Herbert Beever
- 👤 Yeon Fong Liang
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-02 12:44
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/40; H10W74/47; C; C08; C08L; C08L81/00; C08L81/02; C08L23/00; C08L33/00; C08L33/04; C08L33/06; C08L33/08; C08L83/00; C08L83/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
27 words
A molding composition comprising poly(arylene sulfide), characterized b y containing a polymeric rubber selected from silicone rubber, ethylene-acrylic rubber, ethylene-propylene rubber, ethylene-propylene-diene rubber and poly(butyl acrylate) rubber.
Claim 2
Dependent Claim
27 words
A molding composition comprising poly(arylene sulfide), characterized b y containing a polymeric rubber selected from silicone rubber, ethylene-acrylic rubber, ethylene-propylene rubber, ethylene-propylene-diene rubber and poly(butyl acrylate) rubber.
Claim 3
Dependent Claim
23 words
The composition of claim 1 characterized in that the amount of polymeric rubber is from 0.1 to 40 weight percent of the composition.
Claim 4
Dependent Claim
14 words
The composition of claim 1 characterized in that the polymeric rubber is silicone rubber.
Claim 5
Dependent Claim
24 words
The composition of claim 3 characterized in that the amount of silicone rubber is from 0.5 to 10 weight percent of the total composition.
Claim 6
Dependent Claim
14 words
The composition of claim 1 characterized in that the polymeric rubber is ethylene-acrylic rubber.
Claim 7
Dependent Claim
14 words
The composition of claim 1 characterized in that the polymeric rubber is ethylene-propylene rubber.
Claim 8
Dependent Claim
25 words
The composition of claim 5 or 6 characterized in that the amount of rubber is from 0.5 to 15 weight percent of the total composition.
Claim 9
Dependent Claim
15 words
The composition of claim 1 characterized in that the polymeric rubber is poly(butyl acrylate) rubber.
Claim 10
Dependent Claim
14 words
The composition of claim 1 characterized in that the polymeric rubber is ethylene-propylene-diene rubber.
Claim 11
Dependent Claim
25 words
The composition of claim 8 or 9 characterized in that the amount of rubber is from 0.5 to 25 weight percent of the total composition.
Claim 12
Dependent Claim
41 words
The composition of claims 3 or 8 characterized by also containing up to about 3 weight percent of the total composition of organosilane; in particular wherein the amount of organosilane is from 0.1 to 2 weight percent of the total composition.
Claim 13
Dependent Claim
15 words
Use of the composition of any of claims 1 to11 for pro-5 ducing molded articles.