Silicon aluminium oxynitride ceramic product and method of production
Assignee: Cookson Syalons Ltd
•
Filing: 1984-02-06
•
Granted: —
•
Expires: 2004-02-06
Abstract
Abstract A silicon aluminium oxynitride product having the crystal lattice structure of silicon oxynitride but of expanded cell dimensions is produced by sintering a powder mixture of 50 to 65 wt% of Si 3 N 4 , 22 to 35 wt% Si0 2 , 1 to 20 wt% Al 2 O 3 and 1 to 15 wt% of at least one oxide of Y, Li, Mg, Ca, Sc, Ce or another rare earth element, the molar ratio of Si0 2 to Si 3 N 4 being greater than 1:1 and the percentages being based on the total weight of the ingredients. Sintering is effected at 1600 to 1900 °C in a non-oxidising atmosphere so that the Al 2 O 3 , said at least one oxide and part of the Si0 2 in the mixture react to form a liquid phase from which silicon aluminium oxynitride having an expanded silicon oxynitride crystal lattice is crystallised. The sintered material is cooled to form a product containing said silicon aluminium oxynitride and at least one grain boundary phase containing silicon and the metal(s) of said at least one oxide.
Inventors
- 👤 Kenneth Henderson Jack
- 👤 Mark Brian Trigg
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-08 14:22
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/597
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
101 words
A silicon aluminium oxynitride product containing from 80% to 98% by weight of 0'-phase silicon aluminium oxynitride as a first phase and 20% to 2% by weight of at least one second phase which contains silicon and at least one metal other than silicon or aluminium, said percentages being based on the total weight of said first and second phases, said product being from about 85% to about 99% of theoretical density and having a microstructure which is a crystallised network of said 0' - phase silicon aluminium oxynitride with said at least one second phase as a grain boundary phase.
Claim 2
Dependent Claim
101 words
A silicon aluminium oxynitride product containing from 80% to 98% by weight of 0'-phase silicon aluminium oxynitride as a first phase and 20% to 2% by weight of at least one second phase which contains silicon and at least one metal other than silicon or aluminium, said percentages being based on the total weight of said first and second phases, said product being from about 85% to about 99% of theoretical density and having a microstructure which is a crystallised network of said 0' - phase silicon aluminium oxynitride with said at least one second phase as a grain boundary phase.
Claim 3
Dependent Claim
20 words
A product as claimed in Claim 1, wherein said first and second phases constitute a major proportion of said product.
Claim 4
Dependent Claim
25 words
A product as claimed in Claim 1, consisting essentially of said first and second phases together with the optional inclusion of an inert dispersed phase.
Claim 5
Dependent Claim
21 words
A product as claimed in Claim 1, wherein said at least one second phase consists of or includes a glass phase.
Claim 6
Dependent Claim
21 words
A product as claimed in Claim 1, wherein said at least one second phase consists of or includes a crystalline phase.
Claim 7
Dependent Claim
48 words
A product as claimed in Claim 1, wherein said metal other than silicon and aluminium is selected such that it reacts with silica and alumina to form a glass phase which is molten during the sintering of said product and from which said O'-phase silicon aluminium oxynitride precipitates.
Claim 8
Dependent Claim
34 words
A product as claimed in Claim 6, wherein said metal other than silicon and aluminium is selected from the group consisting of yttrium, lithium, magnesium, calcium, scandium, cerium and the other rare earth elements.
Claim 9
Independent Claim
182 words
A method of forming a dense ceramic product comprising the steps of forming a powder mixture containing (a) 50% to 65% by weight silicon nitride, (b) 22% to 35% by weight silica, in which the molar ratio of silica to silicon nitride is at least 1:1, (c) 1% to 20% by weight (on an oxide basis) of an oxygen-containing aluminium compound and (d) 1% to 15% by weight (on an oxide basis) of at least one compound selected from oxides, hydroxides, carbonates, oxynitrides, nitrates or silicates of metals other than silicon or aluminium, said percentages being based on the total weight of ingredients (a) to (d); sintering said powder mixture at a temperature of from 1600°C to 1900 0 C in a non-oxidising atmosphere whereby said aluminium compound, said at least one compound and part of said silica in said mixture react to form a liquid phase from which is precipitated O'-phase silicon aluminium oxynitride; and cooling the sintered material to form a product containing said O'-phase silicon aluminium oxynitride and at least one grain boundary phase containing silicon and said metal.
Claim 10
Independent Claim
182 words
A method of forming a dense ceramic product comprising the steps of forming a powder mixture containing (a) 50% to 65% by weight silicon nitride, (b) 22% to 35% by weight silica, in which the molar ratio of silica to silicon nitride is at least 1:1, (c) 1% to 20% by weight (on an oxide basis) of an oxygen-containing aluminium compound and (d) 1% to 15% by weight (on an oxide basis) of at least one compound selected from oxides, hydroxides, carbonates, oxynitrides, nitrates or silicates of metals other than silicon or aluminium, said percentages being based on the total weight of ingredients (a) to (d); sintering said powder mixture at a temperature of from 1600°C to 1900 0 C in a non-oxidising atmosphere whereby said aluminium compound, said at least one compound and part of said silica in said mixture react to form a liquid phase from which is precipitated O'-phase silicon aluminium oxynitride; and cooling the sintered material to form a product containing said O'-phase silicon aluminium oxynitride and at least one grain boundary phase containing silicon and said metal.
Claim 11
Dependent Claim
24 words
A, method as claimed in Claim 8, wherein the molar ratio of silica to silicon nitride in the powder mixture does not exceed 1.5:1.
Claim 12
Dependent Claim
72 words
A method as claimed in Claim 8, wherein said powder mixture contains silicon nitride in an amount of from 50% to 60% by weight, said silica in an amount of from 25% to 30% by weight, said aluminium compound in an amount of from 1.0% to 15% by weight (on an oxide basis) and said at least one compound in an amount from 3% to 12% by weight (on an oxide basis).
Claim 13
Dependent Claim
19 words
A method as claimed in Claim 8, wherein the sintering step is performed in the absence of applied pressure.
Claim 14
Dependent Claim
46 words
A method as claimed in claim 8, wherein said at least one compound is selected so as to react with part of the silica and the oxide of aluminium to give, during reaction, an alumino silicate of. said metal which is molten at the sintering temperature.
Claim 15
Dependent Claim
19 words
A method as claimed in Claim 12, wherein said molten alumino silicate of said metal(s) also contains combined nitrogen.
Claim 16
Dependent Claim
36 words
A method as claimed in Claim 8, wherein the cooling step is effected naturally to room temperature to ensure that a second phase comprising a glass containing silicon, aluminium and said metal(s) exists in said product.
Claim 17
Dependent Claim
38 words
A method as claimed in Claim 14, wherein after said cooling step, the product is heat treated by reheating it to a temperature of the order of 1000°C to 1400°C to cause the glass phase to be devitrified.
Claim 18
Dependent Claim
25 words
A method as claimed in Claim 8, wherein the cooling step is effected at a sufficiently slow rate to cause the glass to be devitrified.
Claim 19
Dependent Claim
15 words
A method as claimed in Claim 16, wherein the cooling rate is less than 100°C/hr.
Claim 20
Dependent Claim
46 words
A method as claimed in Claim 8, wherein said metal of said at least one compound is yttrium, lithium, magnesium, calcium, scandium, cerium or another rare earth element, and said compound is the oxide or a compound which decomposes to the oxide at the sintering temperature.
Claim 21
Dependent Claim
39 words
A method as claimed in Claim 8, wherein said at least one compound is reacted with part of the silica to produce a vitreous or crystalline compound prior to reaction with the remaining components to obtain the required products.
Claim 22
Dependent Claim
38 words
A method as claimed in Claim 8, wherein said at least one compound is reacted with silica and alumina to produce a vitreous or crystalline compound prior to reaction with the remaining components to obtain the required products.
Claim 23
Dependent Claim
44 words
21 A method as claimed in Claim 8, wherein said at least one compound is yttria and the silica and yttria are reacted together in a molar ratio of 2:1 to form yttrium silicate which is included in the mixture before the sintering step.
Claim 24
Dependent Claim
70 words
A method as claimed in Claim 8, wherein the product contains from 80% to 98% by weight of said 0'-phase silicon aluminium oxynitride as a first phase and 20% to 2% by weight of said at least one grain boundary phase, said percentages being based on the total weight of said phases, and wherein said product has a density of from about 85% to about 99% of the theoretical density.
Claim 25
Dependent Claim
17 words
A method as claimed in Claim 22, wherein said phases constitute a major proportion of said product.
Claim 26
Dependent Claim
25 words
A method as claimed in Claim 22, wherein said product consists essentially of said phases together with the optional inclusion of an inert dispersed phase.
References Cited (Backward Citations)
US4365022A
Cited
EP0087888A2
Cited
USPTO Annuity & Maintenance Windows
Maintenance schedule is calculated for granted US utility patents.