EP0080908A1
Expired / Lapsed
EP
⏱️ 0.0 years remaining
One step anticoagulant coating
Assignee: Becton Dickinson and Co
•
Filing: 1982-12-02
•
Granted: —
•
Expires: 2002-12-02
Abstract
Abstract This invention relates to single-step coating methods for coating substrates such as plastics or glass to impart properties to the substrate which are anticoagulant and hydrophobic, and to substrates so coated. The method is particularly useful in coating the internal surfaces of blood test vessels, such as microcontainers or VACUTAINERS R for receiving blood samples for subsequent testing. The method herein imparts the desired properties to the vessel in a single step by combining silicone containing material in a water vehicle to which has been added a quantity of an anticoagulant, such as heparin or ethylene diamine tetraacetic acid (EDTA), followed by air drying.
Inventors
- 👤 James A. Burns
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-10-26 04:25
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/28; C03C17/30; A; A61; A61L; A61L33/00; A61L33/0005; A61L33/0011; A61L33/0041; Y; Y10; Y10S; Y10S215/00; Y10S215/03; Y10S623/00; Y10S623/92
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
92 words
A method for coating substrates which coating readily dissolves in blood to provide simultaneously an anticoagulant property and a hydrophobic property, characterized by the steps of (a) preparing a coating solution comprising admixing (1) a liquid vehicle for said solution; (2) a member selected from the group consisting of a heparin compound and ethylene diamine tetraacetic acid; and (3) a silicone containing material; (b) selecting a substrate to be coated; (c) applying said coating solution from said preparing step to said substrate from said selecting step; and (d) drying said applied coating.
Claim 2
Independent Claim
92 words
A method for coating substrates which coating readily dissolves in blood to provide simultaneously an anticoagulant property and a hydrophobic property, characterized by the steps of (a) preparing a coating solution comprising admixing (1) a liquid vehicle for said solution; (2) a member selected from the group consisting of a heparin compound and ethylene diamine tetraacetic acid; and (3) a silicone containing material; (b) selecting a substrate to be coated; (c) applying said coating solution from said preparing step to said substrate from said selecting step; and (d) drying said applied coating.
Claim 3
Dependent Claim
28 words
The method of Claim 1, further characterized by (a) said liquid vehicle in said preparing step is deionized water, and (b) said silicone containing material is an organopolysiloxane.
Claim 4
Dependent Claim
30 words
The method of Claim 1, further characterized by (a) said substrate is a member selected from the group consisting of glass, polyethylene, polypropylene, polystyrene, acrylonitrile-butadienestyrene terpolymer, an acetal, and nylon.
Claim 5
Dependent Claim
42 words
The method of Claim 1, further characterized by (a).said drying step being carried out by applying an air jet to the coated substrate at an elevated temperature for a period of time within the range of between about 5 and 20 seconds.
Claim 6
Dependent Claim
27 words
The method of Claim 4, further characterized by (a) said drying step being carried out at a temperature within the range of between about 175°F and 225°F.
Claim 7
Dependent Claim
20 words
The method of Claim 5, further characterized by (a) said temperature is about 200°F, and said time is 12 seconds.
Claim 8
Dependent Claim
65 words
The method of Claim 1, further characterized by (a) said preparing step is carried out by admixing by weight (1) within the range of between about 98.208 parts and 98.802 parts deionized water; (2) within the range of between about 0.9920 parts and 0.9980 parts of a silicone containing material; and (3) within the range of between about 0.2 parts and 0.8 parts ammonium heparin.
Claim 9
Dependent Claim
56 words
The method of Claim 7, further characterized by (a) said ammonium heparin is present within the range of between about 0.5 parts and 0.55 parts: (b) said silicone containing material is present within the range of between about 0.9945 parts and 0.9950 parts; and (c) said deionized water is present within 98.4555 parts and 98.505 parts.
Claim 10
Dependent Claim
65 words
The method of Claim 1, further characterized by (a) said preparing step is carried out by admixing by weight (1) within the range of between about 94.05 and 97.614 parts deionized water; (2) within the range of between about 1.4 parts and 5 parts sodium ethylene diamine tetraacetic acid; and (3) within the range of between about 0.950 and 0.986 parts said silicone containing material.
Claim 11
Dependent Claim
61 words
The method of Claim 9, further characterized by (a) said sodium ethylene diamine tetraacetic acid is present within the range of between about 3.1 and 5 parts; (b) said silicone containing material is present within the range of between about 0.950 and 0.969 parts; and (c) said deionized water is present within the range of between about 94.05 and 95.931 parts.
Claim 12
Dependent Claim
87 words
A substrate characterized by a coating with anticoagulant and hydrophobic properties which readily dissolves in blood, obtained by the steps of (a) preparing a coating solution comprising admixing (1) a liquid vehicle for said solution; (2) a member selected from the group consisting of a heparin compound and ethylene diamine tetraacetic acid; and (3) a silicone containing material (b) selecting a substrate to be coated; (c) applying said coating solution from said preparing step to said substrate from said selecting step; and (d) drying said applied coating.
Claim 13
Dependent Claim
87 words
A substrate characterized by a coating with anticoagulant and hydrophobic properties which readily dissolves in blood, obtained by the steps of (a) preparing a coating solution comprising admixing (1) a liquid vehicle for said solution; (2) a member selected from the group consisting of a heparin compound and ethylene diamine tetraacetic acid; and (3) a silicone containing material (b) selecting a substrate to be coated; (c) applying said coating solution from said preparing step to said substrate from said selecting step; and (d) drying said applied coating.
References Cited (Backward Citations)
GB1159659A
Cited
CH496482A
Cited
FR2114230A5
Cited
FR2142277A5
Cited
DE2647389A1
Cited
US4112925A
Cited
EP0054919A2
Cited