Transparent coating composition for antistatic use
Assignee: Mitsubishi Materials Corp
•
Filing: 1981-11-13
•
Granted: —
•
Expires: 2001-11-13
Abstract
Abstract Tin oxide containing 0.1 to 20 wt% antimony (Sb) is almost white and shows excellent conductivity. A coating composition for antistatic use is obtained by mixing powder of this Sb-containing tin oxide having a particle size of 0.4 pm or less with a binder resin in a definite proportion. This coating composition can be applied to non-conductive substrates of electronic or electric parts, construction materials or the like to give an antistatic effect without spoiling the color tone of the substrates.
Inventors
- 👤 Motohiko Yoshizumi
Bibliographic Details
Application Number
—
Jurisdiction
EP
Data Source
google_patents
Last Synchronized
2026-11-05 22:57
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; C; C09; C09C; C09C1/00; C09C1/0081; C09D; C09D5/00; C09D5/24; C09K; C09K3/00; C09K3/16; H10; H10W; H10W42/00; H10W42/60; C01; C01P; C01P2004/00; C01P2004/60; C01P2004/62; C01P2004/80; C01P2004/82; C01P2004/84; C01P2004/86; C01P2006/00; C01P2006/12; C01P2006/32; C01P2006/40; C01P2006/60; C01P2006/80; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
59 words
An antistatic, transparent coating composition comprising a binder resin and an electroconductive powder of 5 to 90% by weight based on the total quantity of said binder resin and said powder, said electroconductive powder comprising an antimony-containing tin oxide wherein the antimony content is 0.1 to 20% by weight and having a particle size of 0.4 µm or less.
Claim 2
Dependent Claim
59 words
An antistatic, transparent coating composition comprising a binder resin and an electroconductive powder of 5 to 90% by weight based on the total quantity of said binder resin and said powder, said electroconductive powder comprising an antimony-containing tin oxide wherein the antimony content is 0.1 to 20% by weight and having a particle size of 0.4 µm or less.
Claim 3
Dependent Claim
29 words
A composition according to Claim 1 wherein the content of the electroconductive powder is 40 to 80% based on the total quantity of the powder and the binder resin.
Claim 4
Dependent Claim
18 words
A composition according to Claim 1 wherein the electroconductive powder contains 2.5 to 20% by weight of antimony.
Claim 5
Dependent Claim
19 words
A composition according to Claim 1 wherein the electroconductive powder has a particle size of 0.2 Pm or less.
Claim 6
Dependent Claim
26 words
A composition according to Claim 1 wherein the electroconductive powder is obtained by co-precipitation from a common solution of an antimony compound and a tin compound.
Claim 7
Dependent Claim
31 words
A composition according to Claim 5 wherein the electroconductive powder is obtained by adding to water a common solution of antimony chloride and tin chloride and causing co-precipitation through the hydrolysis.
Claim 8
Dependent Claim
25 words
A composition according to Claim 5 or 6 wherein the electroconductive powder, after co-precipitation, is further calcinated in an oxidizing atmosphere at 400 to 600°C.
Claim 9
Dependent Claim
49 words
A composition according to Claim 1 which contains a dispersing agent selected from the group consisting of an anionic surfactant, a silane coupling agent, and a titan coupling agent in a quantity of 0.5 to 10 parts by weight based on 100 parts by weight of the electroconductive powder.
Claim 10
Dependent Claim
32 words
A composition according to claim 1 wherein the binder resin is selected from an acrylic resin, a polyester resin, a polyurethane resin, a polyvinyl chloride resin, a polycarbonate resin, and a polypropylene.
Claim 11
Dependent Claim
34 words
A composition according to Claim 1 which contains, in addition to the binder resin, a solvent or a dispersion . medium for the binder resin and has a viscosity of 5 to 200 poises.
Claim 12
Dependent Claim
26 words
A method for applying an antistatic treatment to a nonconductive base material which comprises applying the coating composition of Claim 1 on the nonconductive base material.
Claim 13
Dependent Claim
28 words
A method according to Claim 11 wherein the coating composition is applied on the base material in a quantity of 1 to 20 g/m 2 (as a solid).